ASPC MFI3313

ASPC MFI3313


1 product description
MFI3313 is a medium density polyethylene, which has a broad molecular weight distribution and high melt strength. This product specially designed for producing thin films with high tear resistance, good sealability, high strength and high draw down.
2 applications

MFI3313 is recommended for blown film extrusion. This product is suitable for manufacture of high strength carrier bags and high quality thin films for uni/multi-wall packaging.

3 PRODUCT PROPERTIES

Extruder temperature profile: 180-240°C

Frost line height: 6-8 times die diameter.

Blow Up Ratio: 3-5

Recommended film thickness: 10 to 50 μm.

Please note that, these processing conditions are recommended by producer (for 100% MFI3313 resin, not in the case of blending with any other compatible material) , but because of the many particular factors which are outside our knowledge and control, and may affect the use of product, no warranty is given.

4 TOXICITY AND SAFETY

For more detailed information on handling, storage, safety parameters, refer to relevant SDS of Components.

Property

 Value (1)

unit

Test method

 

 

 

Physical Properties

933

 

 

Density (23 oC)

kg/m3

ISO 1183

MFI (190 oC /2.16Kg)

0.1

dg/min

ISO 1133

MFI (190 oC /21.6Kg)

13

dg/min

ISO 1133

Mechanical properties (2)

620

 

 

Tensile Modulus of elasticity

MPa

ISO527-1;2

Max. Tensile Strength (MD)

55

MPa

ISO 527-1;3

Max. Tensile Strength (TD)

43

MPa

ISO 527-1;3

Tensile Strain at Break (MD)

600

%

ISO 527-1

Tensile Strain at Break (TD)

600

%

ISO 527-1

Elemendorf tear strength(MD)

330

mN

ISO 6383-2

Elemendorf tear strength(TD)

2000

mN

ISO 6383-2

Failure energy

8.5

J/mm

DIN 53373

Dart Drop Impact

160

g

ASTM D 1709

Thermal Properties

124

 

 

Melting Point

oC

ISO 3146

Vicat Temp , (A50,50 oC /h , 10 N)

116

oC

ISO 306

Additive : Antioxidant-Heat stabilizer

 

 

 

Notes:

(1)Typical Values: not to be construed as specifications limits.

(2)Properties are based on 20 μm blown film produced at a melt temperature of 220°C and 4 BUR using 100% MFI3313.

Note: this information is based on our current knowledge and experience .in view of many factors that may affect processing and application, this data does not relive processors from the responsibility of carrying out their own tests and experiments, neither does it imply any legally binding assurance of certain properties or of suitability for a specific purpose. It is the responsibility of those to whom we supply our products to ensure that any proprietary rights and existing laws and legislation are observed.