Tabriz-LL0220KJ

Tabriz-LL0220KJ


1 product description
 LL0220KJ are linear low density polyethylene copolymers containing butane-1 as the comonomer. In lean blends, this resin offer greater drawdown compared to LDPE neat and produced Films are tough with better tear resistance, high tensile stress and good hot-tack properties. LL0220KJ offers high slip film with easy opening properties when used pure in thickness rang35-100µm. Addition of other polymers or use other thickness may alter film slip and antiblock performance.
2 applications

.

Property Test Method Unit Typical Value
Physical Properties
MFI(190°C/ 2.16Kg) ASTM D 1238 gr/10Min 2.3
MFI(190°C / 21.6Kg) -
Density ASTM D 1505 gr/cm³ 0.920
Optical Properties
Haze ASTM D 1003 % 12
Gloss (45°) ASTM D 2457 % 95
Formulation
Anti Oxidant Yes
Anti Block Yes
Slip Agent Yes
Mechanical Properties
Dart Drop Impact ASTM D 1709(A) g 90
Tear Strength MD/TD ASTM D 1922 gr/25um 80/35
Tensil Strength at yield MD/TD ASTM D 882 MPa 10/11
Tensil Strength at Break MD/TD ASTM D 882 MPa 30/25
Elongation at Break MD/TD ASTM D 882 % 1000/1100
Secant Modulud ASTM D 882 MPa 195/205
Punctrue Resistance BPC N.Cm 800
Cofficient of friction  ASTM D 1894 > 0.5
Thermal Properties
Vicat Softening Temperature ASTM D 1525 °C 100