Tabriz-LL0220KJ
Tabriz-LL0220KJ
1 product description
LL0220KJ are linear low density polyethylene copolymers containing butane-1 as
the comonomer. In lean blends, this resin offer greater drawdown compared to
LDPE neat and produced Films are tough with better tear resistance, high tensile
stress and good hot-tack properties.
LL0220KJ offers high slip film with easy opening properties when used pure in
thickness rang35-100µm. Addition of other polymers or use other thickness may
alter film slip and antiblock performance.
2 applications
.
| Property | Test Method | Unit | Typical Value |
| Physical Properties | |||
| MFI(190°C/ 2.16Kg) | ASTM D 1238 | gr/10Min | 2.3 |
| MFI(190°C / 21.6Kg) | - | ||
| Density | ASTM D 1505 | gr/cm³ | 0.920 |
| Optical Properties | |||
| Haze | ASTM D 1003 | % | 12 |
| Gloss (45°) | ASTM D 2457 | % | 95 |
| Formulation | |||
| Anti Oxidant | Yes | ||
| Anti Block | Yes | ||
| Slip Agent | Yes | ||
| Mechanical Properties | |||
| Dart Drop Impact | ASTM D 1709(A) | g | 90 |
| Tear Strength MD/TD | ASTM D 1922 | gr/25um | 80/35 |
| Tensil Strength at yield MD/TD | ASTM D 882 | MPa | 10/11 |
| Tensil Strength at Break MD/TD | ASTM D 882 | MPa | 30/25 |
| Elongation at Break MD/TD | ASTM D 882 | % | 1000/1100 |
| Secant Modulud | ASTM D 882 | MPa | 195/205 |
| Punctrue Resistance | BPC | N.Cm | 800 |
| Cofficient of friction | ASTM D 1894 | > 0.5 | |
| Thermal Properties | |||
| Vicat Softening Temperature | ASTM D 1525 | °C | 100 |