SAN-5
SAN-5
1 Classification
General grade
2 Characteristic
- super high strength
- high chemical resistance
3 Application
- ABS Compounding
- disposable lighter
- pounding
- Electrical &electronic parts
| Property | Test method (ASTM) | Test condition | Unit | Typical Value | ABS-28 Specification |
| Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 2 | Min 2.5 |
| Melt flow index | D-1238 |
220ºc , 10 kg |
gr/10 min |
5.5 |
3-7 |
| Rock well hardness | D-785 | ........ | R-scale | 92 | Min90 |
| HDT | D-648 | 1.82 m pa | ºc | 94 | Min 90 |
| Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 110 | Min 99 |
| Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 900 | Min 800 |
| Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 1150 | Min 1250 |
| Flexural strength | D-790 | 23ºc , 50 mm/min | Kg/cm² | 33500 | Min 33000 |
| Flexural Modulus | D-790 | 23ºc , 50 mm/min | Kg/cm² | 0.3 | 0.3 |
| Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 |
| Molding Shrinkage | D-955 | … | % | 0.2~0.6 | 0.2~0.6 |
| Flammability | Ul94 | 1/8inch(3.2mm) | … | HB | HB |
TYPICAL SAN PROCESSING CONDITIONS:
DRYING: it is recommended that GBPC SAN Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin. A moisture level of ≤0.1% should be reached before injection molding the resin.
Some modifications may be required depending on the specific molding equipment and part configuration.
INJECTION MOLDIN
| Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp (°c) | Melt Temp (°c) |
| 190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 |
| Mold Temp (°c) | Filling Speed | |||
| 60-80 | Slow-Med |