SAN2
SAN2
1 Classification
General grade
2 Characteristic
high flow, high transparency
3 Application
- ABS Compounding
- office application
- Cups
- cosmetic container
- Blower fan
- pencil case
- juicer
![](/uploads/posts/2019-03/thumbs/1552986368_3.jpg)
![](/uploads/posts/2019-03/medium/1552986346_2.png)
Property | Test method (ASTM) | Test condition | Unit | Typical Value | ABS-28 Specification |
Izod impact | D-256 | 6.4 mm , notched | Kj/m² | 1 | Min 1 |
Melt flow index | D-1238 |
220ºc , 10 kg |
gr/10 min |
22 |
19-24 |
Rock well hardness | D-785 | ........ | R-scale | 84 | Min82 |
HDT | D-648 | 1.82 m pa | ºc | 90 | Min 87 |
Vicat softening Temp | D-1525 | 5kg/50°c | ºc | 103 | Min 96 |
Tensile strength | D-638 | 23ºc , 50 mm/min | Kg/cm² | 670 | Min 630 |
Tensile elongation | D-638 | 23ºc , 50 mm/min | % | 750 | Min 700 |
Flexural strength | D-790 | 23ºc , 50 mm/min | Kg/cm² | 31500 | Min 31000 |
Flexural Modulus | D-790 | 23ºc , 50 mm/min | Kg/cm² | 0.3 | 0.3 |
Specific Gravity | D-792 | 23ºc | .. | 1.04 | 1.04 |
Molding Shrinkage | D-955 | … | % | 0.2~0.6 | 0.2~0.6 |
Flammability | Ul94 | 1/8inch(3.2mm) | … | HB | HB |
TYPICAL SAN PROCESSING CONDITIONS
DRYING: it is recommended that GBPC SAN Resins be dried at (80-85°c)for 3 hours.
The following molding conditions are recommended starting point for GBPC ABS Resin
A moisture level of ≤0.1% should be reached before injection molding the resin.
Some modifications may be required depending on the specific molding equipment and part configuration.
INJECTION MOLDIN
Rear Temp(°c) | Center Temp (°c) | Center Temp (°c) | Front Temp (°c) | Nozzle Temp (°c) | Melt Temp (°c) |
190-200 | 200-210 | 210-220 | 210-220 | 215-225 | 230 |
Mold Temp (°c) | Filling Speed | |||
60-80 | Slow-Med |