RG 1104 J
RG 1104 J

1 product description
Homopolymer With Narrow MFR Range and Low Taste & Odour
2 applications

OPP Films-metAllizable (Stenter Frame Process), General Extrusion

3 Processing Method

Extrusion

4 PACKING

PP Bags of 25 kgs, 50 Bags on a Pallet  Shrinked b

PROPERTY TEST METHOD UNIT VALUE
MFR ( 230˚ C/ 2.16 Kg ) ASTM  D1238/L gr/10min 42771
Tensile Modulus of Elasticity (1mm/min) ASTM  D638 MPa 1500
Tensile Strength at Yield (50 mm/min) ASTM  D638 MPa 34
Elongation at Yield(50 mm/min) ASTM  D638 % 9
Notched Charpy Impact at 23˚ ISO 179/ 1eA KJ/m2 4
Notched Charpy Impact at -30˚ ISO 179/ 1eA KJ/m2 42742
Vicat Softening Point, 10N ASTM  D1525 ˚C 154
Ball Indentation Hardness ISO 2039-1 MPa 74
HDT ( 0.46 N/mm2 ) ASTM  D648 ˚C 85
Melting Point , DSC ASTM  D3417 ˚C 163
Density ASTM D792 gr/cm3 0.91

The information in this publication is submitted without prejudice, and is based on our current knowledge and experience and on a limited number of tests.

In view of the many factors that may affect Processing and application, these data do not relieve the receiver of this information from the responsibility of carrying out their own tests and experiments; neither do they imply and legally binding assurance of certain properties or of suitability for a specific purpose of the products made with or on the basis of the information in this publication.