RG 1040 N
RG 1040 N
1 product description
Homopolymer Contains Nucleating Agent and Shows a Good FLowability and Stiffness
2 applications
High Stiffness Thermoforming Applications
3 Processing Method
Extrusion
4 PACKING
PP Bags of 25 kgs, 50 Bags on a Pallet Shrinked b
| PROPERTY | TEST MEtdOD | UNIT | VALUE |
| Tensile Modulus of Elasticity (1mm/min) | ASTM D638 | MPa | 2000 |
| Tensile Strengtd at Yield (50 mm/min) | ASTM D638 | MPa | 40 |
| Elongation at Yield(50 mm/min) | ASTM D638 | % | 7 |
| Notched Charpy Impact at 23˚ | ISO 179/ 1eA | KJ/m2 | 3 |
| Notched Charpy Impact at -30˚ | ISO 179/ 1eA | KJ/m2 | 42740 |
| Vicat Softening Point, 10N | ASTM D1525 | ˚C | 158 |
| Ball Indentation Hardness | ISO 2039-1 | MPa | 93 |
| HDT ( 0.46 N/mm2 ) | ASTM D648 | ˚C | 110 |
| Melting Point , DSC | ASTM D3417 | ˚C | 165 |
| Density | ASTM D792 | gr/cm3 | 0.91 |
| MFR ( 230˚ C/ 2.16 Kg ) | ASTM D1238/L | gr/10min | 12 |
tde information in tdis publication is submitted witdout prejudice, and is based on our current knowledge and experience and on a limited number of tests.
In view of tde many factors tdat may affect Processing and application, tdese data do not relieve tde receiver of tdis information from tde responsibility of carrying out tdeir own tests and experiments; neitder do tdey imply and legally binding assurance of certain properties or of suitability for a specific purpose of tde products made witd or on tde basis of tde information in tdis publication.