ASPC HFI5110
HFI5110 is recommended for blown film extrusion. This product is suitable for manufacture of high strength grocery sacks, shopping bags and high quality thin films for uni/multi-wallpackaging. Films produced with this product can be readily treated and printed to give high quality graphics.
Extruder temperature profile: 200-235°C
Frost line height: 6-8 times die diameter.
Blow Up Ratio: 3-5
Recommended film thickness: 15 to 50 μm
Please note that, these processing conditions are recommended by producer only for 100% HFI5110 resin (not in the case of blending with any other compatible material), but because of the many particular factors which are outside our knowledge and
control, and may affect the use of product, no warranty is given.
For more detailed information on handling, storage, safety parameters, refer to relevant SDS of Components.
|
Properties |
Value (1) |
unit |
Test method |
|
Physical Properties |
|
|
|
|
Density (23 oC) |
951 |
kg/cm3 |
ISO 1183 |
|
MFI (190 oC /21.6Kg) |
10 |
dg/min |
ISO 1133 |
|
Mechanical properties (2) |
|
|
|
|
Tensile Modulus of elasticity |
1050 |
MPa |
ISO527-1;2 |
|
Tensile Strength (MD) |
55 |
MPa |
ISO 527-1;3 |
|
Tensile Strength (TD) |
55 |
MPa |
ISO 527-1;3 |
|
Tensile Strain at Break (MD) |
580 |
% |
ISO 527-1 |
|
Tensile Strain at Break (TD) |
620 |
% |
ISO 527-1 |
|
Tensile stress at Yield |
26 |
MPa |
ISO 527-1 |
|
Tensile strain at Yield |
10 |
% |
ISO 527-1 |
|
Elemendorf tear strength(MD) |
250 |
mN |
ISO 6383-2 |
|
Elemendorf tear strength(TD) |
800 |
mN |
ISO 6383-2 |
|
Thermal Properties |
|
|
|
|
Melting Point |
132 |
oC |
ISO 3146 |
|
Vicat Temperature , (A50,50 oC/h , 10N) |
127 |
oC |
ISO 306 |
|
Additives :Antioxidant –Heat stabilizer |
|
|
|
|
Zinc Stearate |
|
|
|
Notes:
(1)Typical Values: not to be construed as specifications limits.
(2)Properties are based on 20 μm blown film produced at a melt temperature of 220°C and 4 BUR using 100% HFI5110.
Note: this information is based on our current knowledge and experience .in view of many factors that may affect processing and application, this data does not relive processors from the responsibility of carrying out their own tests and experiments, neither does it imply any legally binding assurance of certain properties or of suitability for a specific purpose. It is the responsibility of those to whom we supply our products to ensure that any proprietary rights and existing laws and legislation are observed.