TJPC 1507

 TJPC 1507


1 product description
Styrene-Butadiene Rubber "TJPC 1507" is produced by a technology of cold emulsion copolymerization based on soaps of rosin and fatty acids and contains 23.5% of chemically bonded styrene. It is coagulated by a system of acid and synthetic coagulant and stabilized by a non-staining antioxidant.
2 applications

TJPC 1507 is appropriate for Light colored, translucent products such as sponge, industrial goods, rubberized fabric, and toys. In addition, black products requiring good process ability.

3 CHARACTERSTICS

TJPC 1507 has very good properties such as process ability, abrasion resistance, less tendency to scorching processing.

4 PACKAGING - TRANSPORTATION - STORAGE

35 ±0.5 KG bales wrapped with polyethylene film.

36 bales per crate (1260±18 KG).

TJPC1507 is typically transported in covered road trucks, in covered railway carriages and in standard shipping containers. TJPC 1507 is not a dangerous material to transport.

Product should be stored in sheltered conditions away from direct sunlight away from radiant heating elements and the temperature should not exceed 30°C.

Typical Properties

Units

Values

Test method

Raw Mooney viscosity

MU

32-42

ASTM D1646

Volatile Material

% wt

< 0.75

ASTM D5668

Ash Content

% wt

< 1

ASTM D5667

Organic acids

% wt

4.75 -7

ASTM D5774

Soaps

% wt

< 0.5

ASTM D5774

Bounded styrene

% wt

22.5-24.5

ASTM D5775

Compound Mooney viscosity2

MU

< 75

ASTM D1646

Tensile strength (35 min cured)2

kg/cm2

>220

ASTM D 412

Ultimate elongation (35 min cured)2

%

MM 400

ASTM D 412

300 % Modulus (35 min cured)2

kg/cm2

150 -190

ASTM D 412

The above data is only a typical value and to each shipping lot/delivery a quality certificate including data on properties of the product determined during release control is issued. Scope of the testing which is covered by the quality certificate is each time agreed upon in the sales contract.

2 Compounding formula according ASTM D-3182 & D-3185.