ARAK-LL0209KJ
Typical applications for LL1209AA & LL1209KJ are lamination films and heat sealing layers. Also LL1209KJ is highly recommended for display packaging. LL1209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-blockperformance.
Recommended melt temperature for extrusion is about 180°C-225°C.
LL1209AA & LL1209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.
|
Typical properties |
Test method (ASTM) |
Unit |
Value |
|
MFI@190°C,2.16 kg |
D1238 |
gr/10min |
0.9 |
|
Density |
D2839 |
gr/ml |
0.920 |
|
Vicat Softening Point |
D1525 |
°C |
100 |
|
Film * |
|
|
|
|
Tensile Strength @ Yield ,MD/TD |
D638 |
Mpa |
9.5/9.5 |
|
Elongation@Break, MD/TD |
D638 |
% |
450/800 |
|
Tensile Strength@Break,MD/TD |
D688 |
Mpa |
38/28 |
|
Tear Strength, MD/TD |
D1922 |
gr/25mic |
85/530 |
|
Impact Strength, Dart |
D1709 |
gr |
150 |
|
Haze |
D1003 |
% |
5 |
|
Gloss (45°) |
D2457 |
Rating |
70 |
¾Values shown are averages & are not to be considered as product specifications.
*38 microns, 2:1 Blow ratio / MD=Machine Direction, TD=Transverse Direction