ABS-HM0560

ABS-HM0560


1 product description
HM0560 is one of the high modulus resins that has diversity in both manufacturing methods and material characteristics.This grade has high impact and flexural strength, excellent mechanical properties, chemical resistance, mold ability, dimensional stability and paint ability.
2 applications

watches, toys, cassette recorders and etc.Drying prior to processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of -20°F (-29°C) or below is recommended to achieve a moisture content 0.1%. Typical drying conditions are 2 hours at 180° - 190°F (82° - 88°C). Drying for 4 hours at 160° - 170°F (71°-77°C) is also adequate.

3 Drying

Drying prior to processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of -20°F (-29°C) or below is recommended to achieve a moisture content 0.1%. Typical drying conditions are 2 hours at 180° - 190°F (82° - 88°C). Drying for 4 hours at 160° - 170°F (71°-77°C) is also adequate.

PROPERTY

UNIT

TEST METHOD

TYPICAL VALUE

MELT FLOW INDEX

(200°C/5KG)

GR/10MIN

ASTM D-1238

2.5

IZOD IMPACT STRENGTH

KJ/M2

ASTM D-256

13

VICAT SOFTENING POINT(50N LOAD)

℃

ASTM D-1525

107

BULK DENSITY

KG/M3

-

600

TENSILE STRENGTH AT YEILD

KGF/CM2

ASTM D-638

520

ROCKWELL HARDNESS(AT 23°C)

R.SCALE

ASTM D-785

112

*All above mentioned data are typical values and not to be construed as real specifications.Users should confirm results by their own tests.For more information about guaranteed items, please refer to S.S.S.(Standard Sales Specifications)

pic
Print