ABS-SH0150

ABS-SH0150


1 product description
SH-0150 is a high flow acrylonitrile butadiene styrene (ABS) grade with good toughness, high impact strength, excellent mechanical and low-temperature properties. Exhibits good processability, vacuum formability, chemical resistance and dimensional stability. This grade is suitable for processing by extrusion. Used in vacuum formed general thin sheets and refrigerator liner sheets.
2 applications

Parts with significant impact resistance, general sheets.Drying prior to processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of -20°F (-29°C) or below is recommended to achieve a moisture content 0.1%. Typical drying conditions are 2 hours at 180° - 190°F (82° - 88°C). Drying for 4 hours at 160° - 170°F (71°-77°C) is also adequate.

3 Drying

Drying prior to processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of -20°F (-29°C) or below is recommended to achieve a moisture content 0.1%. Typical drying conditions are 2 hours at 180° - 190°F (82° - 88°C). Drying for 4 hours at 160° - 170°F (71°-77°C) is also adequate.

PROPERTY

UNIT

TEST METHOD

TYPICAL VALUE

MELT FLOW INDEX

(200°C/5KG)

GR/10MIN

ASTM D-1238

1.1

IZOD IMPACT STRENGTH

KJ/M2

ASTM D-256

22

VICAT SOFTENING POINT(50N LOAD)

℃

ASTM D-1525

100

BULK DENSITY

KG/M3

-

600

TENSILE STRENGTH AT YEILD

KGF/CM2

ASTM D-638

420

ROCKWELL HARDNESS(AT 23°C)

R.SCALE

ASTM D-785

107

*All above mentioned data are typical values and not to be construed as real specifications.Users should confirm results by their own tests.For more information about guaranteed items, please refer to S.S.S.(Standard Sales Specifications)