ABS-HR0370

ABS-HR0370


1 product description
Although general purpose ABS have good enough mechanical properties for the practical use in terms of processability, impact strength, etc, its use is sometimes limited at high temperature due to the deformation of its molded products by heat. So High Heat Resistant ABS(HR0370) offers an attractive alternative to general purpose ABS and other engineering plastics making it suitable for the Applications designed for the use at high temperature.
2 applications

Automotive interior, Cockpit module parts, Power window, Switch panel, Pull handle, Console

3 Drying

Drying prior to processing is recommended in a desiccant dehumidifying hopper dryer. An inlet air dew point of -20°F (-29°C) or below is recommended to achieve a moisture content 0.1%. Typical drying conditions are 2 hours at 180° - 190°F (82° - 88°C). Drying for 4 hours at 160° - 170°F (71°-77°C) is also adequate.

PROPERTY

UNIT

TEST METHOD

TYPICAL VALUE

MELT FLOW INDEX

(200°C/5KG)

GR/10MIN

ASTM D-1238

1.2

IZOD IMPACT STRENGTH

KJ/M2

ASTM D-256

17

VICAT SOFTENING POINT(50N LOAD)

℃

ASTM D-1525

102

BULK DENSITY

KG/M3

-

600

TENSILE STRENGTH AT YEILD

KGF/CM2

ASTM D-638

450

ROCKWELL HARDNESS(AT 23°C)

R.SCALE

ASTM D-785

106

*All above mentioned data are typical values and not to be construed as real specifications.Users should confirm results by their own tests.For more information about guaranteed items, please refer to S.S.S.(Standard Sales Specifications)

pic