JAMPILENHP510L(C30S)

 JAMHP510L(C30S)


1 description
″Jampilen HP510L″ is a polypropylene homopolymer with good flow properties and is particularly suitable for the extrusion of film yarn, monofilament, cast film and sheet. ″Jampilen HP510L″ combines outstanding processability with good mechanical properties. Film yarn made of ″Jampilen HP510L″ is used for baler twines, packaging twines and ropes. ″Jampilen HP510L″ is well suited for the production of monofilament used for instance in brush and broom filling and technical applications.
2 Typical Applications
  • properties Homopolymer
  • Baler twines, packaging twines and ropes
  • Brush and broom filling and technical applications Coextruded film for packaging
  • Thin sheet for stationery folders Sheet for thermoforming Straws
  • Gunnies
3 Processing Method
  • Extrusion (Sheet, film yarn, monofilament)
  • Cast film
4 Features
  • Good processability
  • Good mechanical 

TYPICAL PROPERTIES

VALUE

UNIT

METHOD

Physical 

Melt Flow Rate (230 oC, 2.16kg)

6.0

g/10min

ASTM D1238

Density

0.9

g/cm3

ASTM D1505

Mechanical 

Flexural Modulus

1500

MPa

ASTM D790

Tensile Strength at Yield

35

MPa

ASTM D638

Tensile Elongation at Yield

12

%

ASTM D638

Izod Impact Strength (notched) at 23 oC

40

J/m

ASTM D256

Rockwell Hardness

100

R Scale

ASTM D785

Thermal 

Vicat softening point (10N)

154

oC

ASTM D1525

H.D.T. (0.46 Mpa)

94

oC

ASTM D648

Accelerated oven ageing in air at 150 oC

360

hours

ASTM D3012