Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > RG 1002 G
Back | Print

RG 1002 G

RG 1002 G


1 product description
Homopolymer With High Stiffness
2 applications

High Stiffness Thermoformed Parts, Special Extrusion Applications

3 processing

Extrusion

4 features

PP Bags of 25 kgs, 50 Bags on a Pallet  Shrinked b

PROPERTY TEST METHOD UNIT VALUE
MFR ( 230˚ C/ 2.16 Kg ) ASTM  D1238/L gr/10min 0.9
Tensile Modulus of Elasticity (1mm/min) ASTM  D638 MPa 2000
Tensile Strength at Yield (50 mm/min) ASTM  D638 MPa 38
Elongation at Yield(50 mm/min) ASTM  D638 % 7
Notched Charpy Impact at 23˚ ISO 179/ 1eA KJ/m2 4
Notched Charpy Impact at -30˚ ISO 179/ 1eA KJ/m2 42740
Vicat Softening Point, 10N ASTM  D1525 ˚C 158
Ball Indentation Hardness ISO 2039-1 MPa 80
HDT ( 0.46 N/mm2 ) ASTM  D648 ˚C 108
Melting Point , DSC ASTM  D3417 ˚C 165
Density ASTM D792 gr/cm3 0.91

The information in this publication is submitted without prejudice, and is based on our current knowledge and experience and on a limited number of tests.

In view of the many factors that may affect Processing and application, these data do not relieve the receiver of this information from the responsibility of carrying out their own tests and experiments; neither do they imply and legally binding assurance of certain properties or of suitability for a specific purpose of the products made with or on the basis of the information in this publication.