Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > TJPC 1220C
Back | Print

TJPC 1220C

TJPC 1220C


1 product description
High-Cis Polybutadiene rubber "TJPC 1220C" is produced by a technology of solution polymerization based on Ziegler-Natta (Cobalt) catalyst. It has more than 96% of 1,4 Cis content and very low glass transition temperature.
2 applications

TJPC 1220C is appropriate for rubber compounds used in the production of tire, floor coverings, footwear, children toys, rubber hose, belts and golf balls.

3 processing

Cured "TJPC 1220C" has excellent properties such as abrasion resistance, tear strength, resilience, weathering resistance and low rolling resistance (good fuel economy) due to its low glass transition temperature (Tg typically <-90°C).

4 features

35 ±0.5 KG bales wrapped with polyethylene film.

36 bales per crate (1260±18 KG).

TJPC 1220C is typically transported in covered road trucks, in covered railway carriages and in standard shipping containers. TJPC 1220C is not a dangerous material to transport.

Product should be stored in sheltered conditions away from direct sunlight away from radiant heating elements and the temperature should not exceed 30°C.

Typical Properties1

Typical Properties

Units

Values

Test method

Mooney viscosity (ML 1+4 @ 100 0C)

MU

43-53

ASTM D1646

Cis Content

wt%

MIN 96

Internal Method

Volatile Material

wt%

MAX 2

ASTM D1416

Ash Content

wt%

MAX 0.3

ASTM D1416

 

1 To each shipping lot/delivery a quality certificate including data on properties of the product determined during release control is issued. Scope of the testing which is covered by the quality certificate is each time agreed upon in the sales contract.

Typical Properties-Compounds2

Typical Pro

Units

Values

Test method

Compound Mooney Viscosity

MU

MAX 77

ASTM D - 1646

Tensile Strength(35 Min)

Kgf/cm3

MIN 140

ASTM D412

Elongation at Break (35 Min)

%

MIN 420

ASTM D412

300% Modulus at 145 °C

25 Min

Kgf/cm3

65-103

ASTM D412

35 Min

Kgf/cm3

70-105

ASTM D412

50 Min

Kgf/cm3

70-110

ASTM D412

 

2 Compounding formula according ASTM D-3189.

pic