PGPICC TECHNICAL HDPE-7000F
- recommend film thickness at 10-20 micron
- shooing bag and T-shirt bag
- high tensile strength with good dart impact strength
- garbage bag
- low gel content
- liner bag
- good moisture barrier
- enhanced ultra thin film
- food contact applicable
- high stiffness
- good impact resistance and processability
- wide service temperature range, UV resistance
|
PROPERTIES |
Test Method |
Value |
Value |
|
|
Resin Properties |
||||
|
Melt flow rate |
ASTM D 1238 @ 190 °C, 2.16 kg |
0.04 |
g/10 min |
|
|
Density |
ASTM D 1505 |
0.954 |
g/cm3 |
|
|
Melting Point |
ASTM D 2117 |
131 |
°C |
|
|
Vicat Softening Point |
ASTM D 1525 |
124 |
°C |
|
|
Brittleness Temperature |
ASTM D 746 |
< -60 |
°C |
|
|
ESCR |
ASTM D 1693 @ 50 °C |
> 1000 |
hrs,F50 |
|
|
Film Properties |
||||
|
Tensile Strength at yield |
ASTM D 638 @crosshead speed 50 mm /min |
MD:_*,TD:250* |
kg/cm2 |
|
|
Tensile Strength at break |
ASTM D 638 @crosshead speed 50 mm /min |
MD:620*,TD:310* |
kg/cm2 |
|
|
Tensile Modulus, 2% secant |
ASTM D 638 @crosshead speed 50 mm /min |
MD:8200*,TD:8000* |
kg/cm2 |
|
|
Elongation at Break |
ASTM D 638 @crosshead speed 50 mm /min |
MD:240*,TD:450* |
% |
|
|
Elmendorf Tear Strength |
ASTM D 1922 |
MD:3*,TD:80* |
g |
|
|
Dart Impact Strength |
ASTM D 1709 |
139* |
g |
|
(*)Properties obtained from film produced on a pilot line, 12 micron,BUR 5:1, MD Machine Direction, TD= transverse direction note: Conversion factor for changing unit from kg/cm2 to Mpa is divided by 10.2