Tabriz-LL0209KJ
Tabriz-LL0209KJ
1 product description
LL0209KJ are linear low density polyethylene copolymers containing butane-1
as the comonomer. In lean blends, this resin offer greater drawdown
compared to LDPE neat and produced Films are tough with better tear
resistance, high tensile stress and good hot-tack properties.
LL0209KJ offers high slip film with easy opening properties when used pure in
thickness rang 35-100µm. Addition of other polymers or use other thickness
may alter film slip and anti-block performance.
2 applications
.
| Property | Test Method | Unit | Typical Value |
| Physical Properties | |||
| MFI(190°C/ 2.16Kg) | ASTM D 1238 | gr/10Min | 0.9 |
| MFI(190°C / 21.6Kg) | 29.0 | ||
| Density | ASTM D 1505 | gr/cm³ | 0.920 |
| Optical Properties | |||
| Haze | ASTM D 1003 | % | 12 |
| Gloss (45°) | ASTM D 2457 | % | 50 |
| Formulation | |||
| Anti Oxidant | Yes | ||
| UV Stabilizer | Yes | ||
| Slip Agent | Yes | ||
| Mechanical Properties | |||
| Dart Drop Impact | ASTM D 1709(A) | g | 140 |
| Tear Strength MD/TD | ASTM D 1922 | gr/25um | 145/370 |
| Tensil Strength at yield MD/TD | ASTM D 882 | MPa | 10/11 |
| Tensil Strength at Break MD/TD | ASTM D 882 | MPa | 41/32 |
| Elongation at Break MD/TD | ASTM D 882 | % | 620/840 |
| Secant Modulud | ASTM D 882 | MPa | 195/205 |
| Puncture Resistance | BPC | N.Cm | 800 |
| Cofficient of friction | ASTM D 1894 | 0.13 | |
| Thermal Properties | |||
| Vicat Softening Temperature | ASTM D 1525 | °C | 100 |