Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > Marun-X30S
Back | Print

Marun-X30S

Marun-X30S


1 product description
X 30 Sis a homopolymer particularly suited for the extrusion of cast and water quenched blown film. X 30 S is formulated with a general purpose stabilisation package and does not contain any slip or antiblocking agents. X 30 S exhibits excellent pcocessability and outstanding optical properties. This makes X 30 S particularly suitable for film for packaging food-stuffs such as pasta, snacks, biscuits, bakery products and confectionery. Other applications include film for packaging for flowers, books, stationery, blankets, shirts, knitwear and hosiery. X 30 S is also very appropriate for the extrusion of small pipes and drinking straws. X 30 Scan be used for lamination with polyester, polyamide and aluminium for packaging of snacks, crisps, sweets, coffee, meat products and pre-cooked foods. In these applications, X 30 S gives an excellent high gloss finish in laminates and exhibits good printability after Corona treatment. X 30 S can also be coextruded with and VAL TEC heterophasic copolymer grades to produce high gloss finishes on blow moulded pigmented bottles and coextruded sheet
2 applications
  • Values shown are averages and are not to be considered as p roduct specification These values may shift slightly as additional data are accumlsted.
  • ISO test methods are the lates under the societys current procedures. All specimens are prepared by injection moulding . 
PROPERTIES method unit TYPICAL VALUE (a)
Physical properties Melt flow rate (230'C, 2.16 kg) Density

IS01133

ISO 1183

Dg/min

g/cm3

9

0.9

  Mechanical properties Flexural modulus Tensile strength yield Elongation at yield IZOD impact strenghh (notched) at 23°G Hardness Shore D 

ISO 178

ISO R527

ISO R 527

ISO 180

ISO 868

N/mm2

N/mm2

%

kJ/m2

Points

1500

34

13

4

71

Thermal properties Vicat softening point (9.8 N) H.D.T. (0.46 Mpa) Accelerated oven ageing in air (forced circulation) at 150 °C

ISO 306/A

ISO 75/B

ISO 4577

°C

°C

hours

155

115

360

Optical Properties Haze Gloss (45 °G)

MTM 1703 1

MTM 17021

%

%

1

85