Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > SAN-4
Back | Print

SAN-4

SAN-4


1 product description
General grade
2 applications

super high strength

3 processing
  • ABS Compounding
  • disposable lighter
  • pounding
  • Electrical &electronic parts
Property Test method (ASTM) Test condition Unit Typical Value ABS-28 Specification
Izod impact D-256 6.4 mm , notched Kj/m² 36 Min33
Melt flow index D-1238

220ºc , 10 kg

gr/10 min

6.5

4-10

Rock well hardness D-785 ........ R-scale 107 95-115
HDT D-648 1.82 m pa ºc 88 Min84
Vicat softening Temp D-1525 5kg/50°c ºc 98 Min 93
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 445 Min 400
Tensile elongation D-638 23ºc , 50 mm/min % 30 Min 25
Flexural strength D-790 23ºc , 50 mm/min Kg/cm² 640 Min 650
Flexural Modulus D-790 23ºc , 50 mm/min Kg/cm² 21000 Min 18000
Specific Gravity D-792 23ºc .. 1.04 1.04
Molding Shrinkage D-955 % 0.4-0.7 0.4-0.7
Flammability Ul94 1/8inch(3.2mm) HB HB

TYPICAL SAN PROCESSING CONDITIONS:

DRYING: it is recommended that GBPC SAN Resins be dried at (80-85°c)for 3 hours.

The following molding conditions are recommended starting point for GBPC ABS Resin.

A moisture level of ≤0.1% should be reached before injection molding the resin.

Some modifications may be required depending on the specific molding equipment and part configuration.

INJECTION MOLDIN

Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp (°c) Melt Temp (°c)
190-200 200-210 210-220 215-225 215-225 230

Mold Temp (°c) Filling Speed  
60-80 Slow-Med