Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > ABS-GH500
Back | Print

ABS-GH500

ABS-GH500


1 product description
Special grade/ultra high heat resistance
2 applications

Ultra Heat Resistance& No odor

3 processing

Automobile parts and Electronic parts and etc

Property Test method (ASTM) Test condition Unit Typical Value ABS-28 Specification
Izod impact D-256 6.4 mm , notched Kj/m² 16 Min14
Melt flow index D-1238

220ºc , 10 kg

gr/10 min

6

4-10

Rock well hardness D-785 ........ R-scale 110 100-120
HDT D-648 1.82 m pa ºc 110 Min107
Vicat softening Temp D-1525 5kg/50°c ºc 128 Min120
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 470 Min 450
Tensile elongation D-638 23ºc , 50 mm/min % 22 Min 20
Flexural strength D-790 23ºc , 50 mm/min Kg/cm² 700 Min 680
Flexural Modulus D-790 23ºc , 50 mm/min Kg/cm² 23500 Min 20000
Specific Gravity D-792 23ºc .. 1.05 1.05
Molding Shrinkage D-955 % 0.4-0.7 0.4-0.7
Flammability Ul94 1/8inch(3.2mm) HB HB

TYPICAL ABS PROCESSING CONDITIONS:

DRYING: it is recommended that GBPC ABS Heat Resistance Resins be dried at (80-90°c)for 3 hours.

The following molding conditions are recommended starting point for GBPC ABS Resin

Some modifications may be required depending on the specific molding equipment and part configuration.

INJECTION MOLDIN

Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp (°c) Melt Temp (°c)
200-210 210-220 210-220 220-230 220-240 250

Mold Temp (°c) Filling Speed
60-70 Slow-Med