Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > ABS40
Back | Print

ABS40

ABS40


1 product description
General purpose
2 applications

High Impact Resistance

3 processing

Automobile parts(radiator grill &etc.),Helmets,Toys,Suitcase,shoe heels,skis,Golf club heads, Sports equipment,suitcases,&etc

Property Test method (ASTM) Test condition Unit Typical Value ABS-28 Specification
Izod impact D-256 6.4 mm , notched Kj/m² 32 Min26
Melt flow index D-1238

220ºc , 10 kg

gr/10 min

25

18-28

Rock well hardness D-785 ........ R-scale 98 90-110
HDT D-648 1.82 m pa ºc 82 Min82
Vicat softening Temp D-1525 5kg/50°c ºc 92 Min 93
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 400 Min 390
Tensile elongation D-638 23ºc , 50 mm/min % 30 Min 25
Flexural strength D-790 23ºc , 50 mm/min Kg/cm² 580 Min 530
Flexural Modulus D-790 23ºc , 50 mm/min Kg/cm² 18000 Min15000
Specific Gravity D-792 23ºc .. 1.04 1.04
Molding Shrinkage D-955 % 0.4-0.7 0.4-0.7
Flammability Ul94 1/8inch(3.2mm) HB HB

TYPICAL ABS PROCESSING:

DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.

The following molding conditions are recommended starting point for GBPC ABS Resin.

A moisture level of ≤0.1% should be reached before injection molding the resin.

Some modifications may be required depending on the specific molding equipment and part configuration.

INJECTION MOLDIN

Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp (°c) Melt Temp (°c)
190-200 200-210 210-220 210-220 215-225 230

Mold Temp (°c) Filling Speed
60-80 Slow-Med