Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > ABS38
Back | Print

ABS38

ABS38


1 product description
General ABS>Heat Resistance grade
2 applications

Heat Resistance grade

3 processing
  • Mirror housings
  • Hair dryer shells
  • Electric oven exterior parts
  • Atomobile parts

Property Test method (ASTM) Test condition Unit Typical Value ABS-28 Specification
Izod impact D-256 6.4 mm , notched Kj/m² 18 Min16
Melt flow index D-1238

200ºc , 5 kg

220ºc , 10 kg

gr/10 min

0.5

6.5

0.35-0.75

4-10

Rock well hardness D-785 ........ R-scale 110 100-120
HDT D-648 1.82 m pa ºc 100 Min97
Vicat softening Temp D-1525 5kg/50°c ºc 115 Min110
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 460 Min 440
Tensile elongation D-638 23ºc , 50 mm/min % 23 Min 16
Flexural strength D-790 23ºc , 50 mm/min Kg/cm² 670 Min 650
Flexural Modulus D-790 23ºc , 50 mm/min Kg/cm² 22500 Min 20000
Specific Gravity D-792 23ºc .. 1.04 1.04
Molding Shrinkage D-955 % 0.4-0.7 0.4-0.7
Flammability Ul94 1/8inch(3.2mm) HB HB

TYPICAL ABS PROCESSING:

DRYING: it is recommended that GBPC ABS Heat Resistance Resins be dried at (80-90°c)for 3 hours.

A moisture level of ≤0.1% should be reached beforeinjection molding the resin.

The following molding conditions are recommended starting point for GBPC ABS Resin.

Some modifications may be required depending on the specific molding equipment and part configuration.

INJECTION MOLDIN

Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp (°c) Melt Temp (°c)
200-210 210-220 210-220 220-230 230-240 240

Mold Temp (°c) Filling Speed
60-70 Slow-Med
pic