Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > ABS28
Back | Print

ABS28

ABS28


1 product description
General purpose
2 applications

Super high gloss High rigidity

3 processing
  • Electronic and Electrical parts
  • vacuum cleaner
  • washing machine cover
  • Refrigerator door ca

Property Test method (ASTM) Test condition Unit Typical Value ABS-28 Specification
Izod impact D-256 6.4 mm , notched Kj/m² 17 Min16
Melt flow index D-1238 220ºc , 10 kg gr/10 min 35 25-35
Rock well hardness D-785 ........ R-scale 107 105-120
HDT D-648 1.82 m pa ºc 85 Min85
Vicat softening Temp D-1525 5kg/50°c ºc 95 Min95
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 500 Min 440
Tensile elongation D-638 23ºc , 50 mm/min % 15 Min 14
Flexural strength D-790 23ºc , 2.8 mm/min Kg/cm² 680 Min 630
Flexural Modulus D-790 23ºc , 2.8 mm/min Kg/cm² 22500 Min 18500
Specific Gravity D-792 23ºc .. 1.04 1.04
Molding Shrinkage D-955 % 0.4-0.7 0.4-0.7
Flammability Ul94 1/8inch(3.2mm) HB HB

TYPICAL ABS PROCESSING:

CONDITIONS DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours. The following molding conditions are recommended starting point for GBPC ABS Resin.

A moisture level of ≤0.1% should be reached before injection molding the resin.

Some modifications may be required depending on the specific molding equipment and part configuration.

INJECTION MOLDIN

Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp (°c) Melt Temp (°c)
190-200 200-210 210-220 210-220 215-225 230

Mold Temp (°c) Filling Speed
60-80 Slow-Med
pic