Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/classes/templates.class.php on line 165 Deprecated: Array and string offset access syntax with curly braces is deprecated in /home/visionpo/public_html/engine/modules/sitelogin.php on line 101 visionpolymer.ir > Print > ABS10
Back | Print

ABS10

ABS10


1 product description
General grade
2 applications

General plating and electro plating use

  

3 processing
  • Electronic and Electrical parts
  • Automobile parts
  • Refrigerator knobs
  • Cosmetic case

 

Property Test method (ASTM) Test condition Unit Typical value ABS-10 specification
Izod impact D-256 6.4 mm , notched Kj/m² 30 Min24
Melt flow index D-1238 220ºc , 10 kg gr/10 min 32 26-34
Rock well hardness D-785 ........ R-scale 105 95-115
HDT D-648 1.82 m pa ºc 84 Min82
Vicat softening Temp D-1525 5kg/50°c ºc 94 Min 93
Tensile strength D-638 23ºc , 50 mm/min Kg/cm² 420 Min 380
Tensile elongation D-638 23ºc , 50 mm/min % 25 Min 16
Flexural strength D-790 23ºc , 2.8 mm/min Kg/cm² 600 Min 560
Flexural Modulus D-790 23ºc , 2.8 mm/min Kg/cm² 19500 Min17000
Specific Gravity D-792 23ºc .. 1.04 1.04
Molding Shrinkage D-955 % 0.4-0.7 0.4-0.7
Flammability Ul94 1/8inch(3.2mm) HB HB

TYPICAL ABS PROCESSING CONDITIONS:

DRYING: it is recommended that GBPC ABS Resins be dried at (80-85°c)for 3 hours.

The following molding conditions are recommendedbe required depending on the specific molding equipment and part configuration

INJECTION MOLDIN

Rear Temp(°c) Center Temp (°c) Center Temp (°c) Front Temp (°c) Nozzle Temp (°c) Melt Temp (°c)
190-200 200-210 210-220 210-220 215-225 230

Mold Temp (°c) Filling Speed
60-80 Slow-Med